鑄造缺陷名稱分類大全（中英文對照）六

I. 組織缺陷 （鑄鐵 )

球化不良 poor nodularity ,degenerated graphite

蠕墨化不良 degenerated graphite

異常石墨 abnormal graphite

開花狀石墨 exploded graphite

過冷石墨 under cooled graphite ,D-type graphite

石墨細小顆粒 chunky graphite

石墨粗大 kish graphite , kish

整列石墨 aligned graphite

石墨漂浮 floated graphite

石墨魏氏組織 Widmannstatten graphite

麻口 mottled cast iron , mottle

灰點 mottle

反麻口 inverse mottle ( 與麻口相反，在薄斷面處和尖角處形成的麻口）

白口 chill

反白口 reverse chill , inversechill

冷豆 extruded bead , exudation, internal sweating

退火不足 miss annealing , incompleteannealing

粗大枝晶組織 coarsened dendritic

反偏析 inverse segregation

比重偏析 gravity segregation

溶質(zhì)偏析 solute segregation

宏觀偏析 macroscopic segregation

微觀偏析 microscopic segregation

J. 斷口缺陷

表面鐵素體 ferrite rim

表面珠光體 pearlite rim

白緣，脫碳 pearlitic rim , pictureframe , pearlite layer

不均勻斷口 heterogeneous fracturedsurface

破碎激冷層 scattered chill structure ,cold flakes

晶粒粗大 rough grain

尖釘狀斷口 spiky fractured surface

冰糖狀斷口 rock candy fracture surface

K. 力學性能缺陷

硬點 hard spot ( 對鑄件，硬點是硬區(qū)、白口或冷豆等力學性能缺陷的總稱；對鋁合金，硬點是鑄件內(nèi)各種高硬度相，如初晶Si相、金屬間化合物、氧化物，偏析等總稱）

硬度不良 poor hardness , too high orlow hardness

L. 使用性能缺陷

腐蝕性不良 poor corrosion resistance

切削性不良 poor machinability

麻點 torn surface

鋅晶間腐蝕 zinc intergranularcorrosion

電導率不良 poor electricalconductivity

M. 其他缺陷

殘留飛翅 residual fin

殘留黑皮 residual black skin

澆道冒口斷口缺肉 broken casting at gate ,riser or vent

端部缺肉 inside cut

切口缺肉（ 壓鑄件 ） inside cut

翹曲 ( 噴丸引起） camber , excessive cleaning

鑄件彎曲 ( 鑄件變形） warped casting , casting distortion , deformed mold , mold creep

打磨缺肉 crow’s feet

N．鑄造管理缺陷

裂紋 crack

壓痕 impression

O．殘留物

型砂殘留 sand inclusions

噴丸粒殘留 residual shot

鋅蒸汽向爐壁滲透 zinc infiltration intorefractory